Late-Age Properties of Concrete with Different Binders Cured under 45°C at Early Ages

It is commonly accepted that high curing temperature (near 60°C or above) results in reduced mechanical properties and durability of concrete compared to normal curing temperature. The internal temperature of concrete structures at early ages is not so high as 60°C in many circumstances. In this paper, concretes were cured at 45°C at early ages and their late-age properties were studied. The concrete cured at 20°C was employed as the reference sample. Four different concretes were used: plain cement concrete, concrete containing fly ash, concrete containing ground granulate blast furnace slag (GGBS), and concrete containing silica fume. The results show that, for each concrete, high-temperature curing after precuring does not have any adverse effect on the nonevaporable water content, compressive strength, permeability to chloride ions, and the connected porosity of concrete at late ages compared with standard curing. Additionally, high-temperature curing improves the late-age properties of concrete containing fly ash and GGBS.

from #AlexandrosSfakianakis via Alexandros G.Sfakianakis on Inoreader http://ift.tt/2n6rEve
via IFTTT