Ageing Effects on Microstructure, Mechanical Properties, and Fracture Behaviour of 9Cr-1.5Mo-1Co-VNbBN Martensitic Steel Welded Joint for High Temperature Application

This paper deals with long-term ageing effects of 9Cr-1.5Mo-1Co-VNbBN (CB2) steel weldment on its impact toughness, creep rupture behaviour, and hardness in relation to microstructure and fracture characteristics. The weldment was studied in PWHT state and after isothermal expositions at 625°C for 10000 and 30000 hours. Microstructure evolution was studied using analytical scanning and transmission electron microscopy. Charpy V-notch impact toughness tests were performed for all heat-treated states with a notch location in distinct weld regions such as weld metal (WM), heat-affected zone (HAZ), and base material (BM). The overheated HAZ region exhibited the lowest impact toughness as a result of severe welding induced microstructure degradation. Creep tests were performed at 625°C in the stress range between 80 and 120 MPa. At the highest applied stress, creep fracture occurred in WM, whereas at lower stresses the failure position shifted towards fusion zone at WM/HAZ interface. The hardness profiles experienced significant scattering due to weld microstructural heterogeneity. The major fracture mechanisms involved transgranular quasi cleavage and intergranular creep cracking in impact and creep loading conditions, respectively.

from #AlexandrosSfakianakis via Alexandros G.Sfakianakis on Inoreader http://ift.tt/2kN421H
via IFTTT