Efficacy of fluoride varnishes for preventing enamel demineralization after interproximal enamel reduction. Qualitative and quantitative evaluation

by Ascensión Vicente, Antonio José Ortiz Ruiz, Belén Manuela González Paz, José García López, Luis-Alberto Bravo-González

Objectives

To evaluate quantitatively and qualitatively the changes produced to enamel after interproximal reduction and subjected to demineralization cycles, after applying a fluoride varnish (Profluorid) and a fluoride varnish containing tricalcium phosphate modified by fumaric acid (Clinpro White).

Materials and methods

138 interproximal dental surfaces were divided into six groups: 1) Intact enamel; 2) Intact enamel + demineralization cycles (DC); 3) Interproximal Reduction (IR); 4) IR + DC; 5) IR + Profluorid + DC; 6) IR + Clinpro White + DC. IR was performed with a 0.5 mm cylindrical diamond bur. The weight percentage of calcium (Ca), phosphorous (P) and fluoride (F) were quantified by energy-dispersive X-ray spectrometry (EDX). Samples were examined under scanning electron microscopy (SEM).

Results

The weight percentage of Ca was significantly higher (p0.05). The weight percentage of P was similar among all six groups (p>0.05). F was detected on 65% of Group 6 surfaces. SEM images of Groups 4 and 6 showed signs of demineralization, while Group 5 did not.

Conclusions

Profluorid application acts as a barrier against the demineralization of interproximally reduced enamel.