Abstract
Renewed interest has been established in the preparation of silicon nanoparticles for electronic device applications. In this work, we report on the production of silicon powders using a simple ball mill and of silicon nanocomposite ink for screen-printable photovoltaic device on a flexible substrate. Bulk single crystalline silicon was milled for 25 h in the ball mill. The structural properties of the produced silicon nanoparticles were investigated using X-ray diffraction (XRD) and transmission electron microscopy. The results show that the particles remained highly crystalline, though transformed from their original single crystalline state to polycrystalline. The elemental composition using energy dispersive X-ray florescence spectroscopy (EDXRF) revealed that contamination from iron (Fe) and chromium (Cr) of the milling media and oxygen from the atmosphere were insignificant. The size distribution of the nanoparticles follows a lognormal pattern that ranges from 60 nm to about 1.2 μm and a mean particle size of about 103 nm. Electrical characterization of screen-printed PN structures of the nanocomposite formed by embedding the powder into a suitable water-soluble polymer on Kapton sheet reveals an enhanced photocurrent transport resulting from photo-induced carrier generation in the depletion region with energy greater that the Schottky barrier height at the metal-composite interface.
http://ift.tt/2sej2cw
Δεν υπάρχουν σχόλια:
Δημοσίευση σχολίου