Comparative study of dental enamel loss after debonding braces by analytical scanning electron microscopy (SEM)

Abstract

Clinical procedures when shear forces are applied to brackets suggest adhesion forces between 2.8 and 10.0 MPa as appropriate. In this study dental enamel was evaluated by scanning electron microscopy (SEM) before and after removing the brackets. Thirty bicuspids (previous prophylaxis) with metallic brackets (Roth Inovation 0.022 GAC), Transbond Plus SEP 3M Unitek adhesive and Transbond XT 3M resin were used. The samples were preserved to 37°C during 24 hr and submited to tangential forces with the Instron Universal machine 1.0 mm/min speed load strength resistance debonding. Also the Adhesive Remanent Index (ARI) test was made, evaluating the bracket base and the bicuspid surface. All the bracket SEM images were processed with AutoCAD to determine the enamel detached area. The average value was 6.86 MPa (SD ± 3.2 MPa). ARI value 1= 63.3%, value 2= 20%, value 3= 13.3% and 33% presented value 0. All those samples with dental enamel loss, presented different situations as fractures, ledges, horizontal, and vertical loss in some cases, and some scratch lines. There is no association between the debonding resistance and enamel presence. Less than half of the remanent adhesive on the dental enamel was present in most of the samples when the ARI test was applied. When the resin area increases, the debonding resistance also increases, and when the enamel loss increases, the resin free metallic area of the bracket base decreases in the debonding.

Bracket detachable at 3.34 MPa (clinically adequate value to avoid damage to the enamel), where we can observe resin (r), lost enamel (e) and mesh metal area (m), as well as edges, fractures and scratch lines in the limit of the enamel loss area.

from #AlexandrosSfakianakis via Alexandros G.Sfakianakis on Inoreader http://ift.tt/2jQ4UT5
via IFTTT